MCA -HA-100

Molecular formula：C6H9N9O3
Molecular weight ：255.24

MCA-HA-100 N-halogen flame retardant fire retardant in the traditional use of sub-word based on the MCA modifier for composite modified to add a new efficient and environmentally friendly polymer flame retardant in plastics can reach nanometer Decentralized level, not used in conjunction with other flame retardants, adding more likely, into carbon better, more efficient flame retardant, low dosage that is able to meet European (UL-94) V-0 flammability category, cost / Performance ratio excellent. Through our unique "super fine and stable modification"process to achieve the flame retardant performance and the perfect combination of safety performance.

 
Features
  1. MCA-HA-100, Department of harmless non-toxic flame retardant, from the processing of health and safety considerations for the most
Good. For the environmental green products.
2. MCA-HA-100 sublimation temperature of 440 ℃, it is in the process, heat resistance, thermal stability
3. The product dispersion characteristics, the use of the product, cost-effective access to superior electrical performance and mechanical properties.
4. Modified MCA-HA-100 after adding synthetic resin products with excellent quality: do not fade, do not spray frost In addition the product can not use other synergistic agent.
5. Modified MCA-HA-100 after adding the product can reduce the resin does not drip or dripping, to
V0 grade.

Features

Appearance: white fine crystalline powder, odorless, tasteless, greasy feel.
Sublimation temperature: 440 ℃ Density: (kg/m3) :1500-1600 Bulk Density: (kg/m3) :450-550 Loss on heating: (760mmHg)
Temperature 0
300 ℃ 5 hours 0
3.5% 350 ℃ 5 CLOCK
Solubility in water: (g/100ml) (20 ℃) 0.001
 
Formulation and operation
  
A. Recommended Recipe:

Formulation and operation

B. out of the data

Extruder speed of charging equipment

Twin-screw (synchronous) 155 r / min Cutting Machine

(Suggested product mix in 1 hour before feeding)

Extruder Set

Note: If a small amount of processed products are dropping, when the compound in the processing of polyester TPU (80A or 90A)
1% -2%, to achieve complete drip.

Area 8 is the vacuum area; 9 area as a gate

Packing, storage

Save